PMMA CAD-CAM discs

POLIDENT PMMA CAD-CAM DISCS are suitable for fabrication of temporary crowns and bridges and for verifying the bridge on the plaster model / in mouth before the final ZrO2 milling process.

temp8 temp8 temp8
Characteristics

Vickers hardness: 26,60 HV. 

Flexural strength: 114 MPa. 

E-Module: 2771 MPa. 

Residual monomer < 1%.

Diameter: 95 – 105 mm. Thickness: 10 – 25 mm.*

*Upon request we can supply also other shapes, diameters and designs.

 

Indications temporary crowns and bridges, verification of the bridge on the plaster model/ mouth Shades A1, A2, A3, B1, B2, B3, BL1, BL2, BL3, CLEAR, enamel colours - E1, E2
photos: 1 | 2 | 3

 
POLIDENT 3-LAYER CAD-CAM DISCS are the ideal product to obtain a perfect colour effect of temporary crowns and bridges with a single step.

temp8 temp8
Characteristics

Vickers hardness: 26,60 HV. 

Flexural strength: 114 MPa. 

E-Module: 2771 MPa. 

Residual monomer < 1%.

Diameter: 95 – 105 mm. Thickness: 10 – 25 mm.

 

Indications temporary crowns and bridges
photos: 1 | 2

 
POLIDENT PINK CAD-CAM DISCS can be used to mill digitally designed highly esthetic and functional dentures.

temp8 temp8 temp8
Characteristics

Discs could be used for immediate load implant denture as a long term provisional in combination with denture teeth and titanium connectors.

The denture bases and other structures are designed in CAD Software.

A 5-Axis milling machine is required, to reach undercut areas.

Artificial teeth are attached on denture base with PMMA resin or light curing composite material with proper primer.

 

MATERIAL:

Polident Pink CAD/CAM discs are made of polymethylmethacrylate (PMMA) with inorganic pigments.

 

CHARACTERISTICS:

Vickers hardness: 26,60 HV.

Flexural strength: 114 MPa.

E-Module: 2771 MPa.

Residual monomer < 1%.

Diameter: 95 – 105 mm.

Thickness: 25, 27, 30 mm.

Indications full dentures, partial dentures Shades pink; new colors available upon request
photos: 1 | 2 | 3

 
POLIDENT CASTING CAD-CAM DISCS can be used for milling castable frameworks for metal casting and castable layers for press ceramic.

temp8 temp8
Characteristics

Produced of 100% organic material that burns-out without any residual ash. 

Diameter: 95 – 105 mm

Thickness: 10 – 25 mm

 

 

Indications milling frameworks for casting
milling castable layers for press ceramic
verifying frameworks on plaster model/ in mouth before final ZrO2 milling (especially recommended for larger ZrO2 frameworks)
Shades transparent
photos: 1 | 2

 
POLIDENT X-RAY CAD-CAM DISCS are X-ray visible discs used for milling diagnostic stents for implant planning.

temp8 temp8 temp8
Characteristics

Contains X- ray visible powder.

Homogeneous mix ensures best visibility.

Prevents light scattering.

 

Indications allows visibility of teeth setup in the x-ray CAT scan for implant planning and determination
photos: 1 | 2 | 3

 
POLIDENT CAD-CAM MODEL DISCS are suitable for milling dental models.

temp8 temp8
Characteristics

The material closed cell structure doesn’t absorb water and is recommended for ceramic layering.

 Available in two densities

A higher density (beige) is easily machinable with CNC milling machines and has an extremely high quality surface finish. With its tight cell structure is especially recommended for milling of stumps/dies.

A lower density (brown) is easily machinable with CNC milling machines and is very light to handle. Recommended for bigger models and antagonist models.

 

Digital models are CAD designed from 3D data acquired with a wide range of digital impressions-taking solutions.

Indications

Milling of stumps/dies, working models and antagonists.

Verifying frameworks on plaster model before final ZrO2 milling (especially recommended for larger ZrO2 frameworks)

photos: 1 | 2

 
print